XPE FOAM MSX15

XPE foam material (Meishuo is the manufacturer of XPE, IXPE foam), is made of low-density polyethylene resin plus crosslinking agent and foaming agent through high-temperature continuous foaming. EPE (physical foamed polyethylene, known as pearl cotton). Tensile strength of XPE foam is higher and the cells are better.

Physical Property Table (TDS):

Product		Crosslinked polyethylene foam
Times		15B
PHYSICAL PROPERTIES		TEST METHOD	METRIC UNITS
Density - Nominal		ISO 845：2006 GB/T 6343-2009	kg/m³	66±8
Shore Hardness	Shore C	LX-C	°	45±5
Size limit	Espesor	Internal	mm	3～8
	Anchura			≤1800
Tensile Strength	TD	ISO 1798：2008 GB/T 6344-2008	MPa	≥400
	MD			≥500
Elongation at Break	TD	ISO 1798：2008 GB/T 6344-2008	%	≥120
	MD			≥120
Tear strength	TD	QB/T 1130-91	KN/m	≥3
	MD			≥3
Dimension Stability (80℃,24h)	TD	ISO 2796：1986 GB/T 8811-2008	%	≤±1.5
	MD			≤±3.0
Water Absorption	under 50% RH condition	ISO 62：2008 GB/T 1034-2008	%	≤0.2
Thermal Conductivity		ISO 8302：1991 GB/T 10294-2008	W/（m.k）	≤0.045